10.8 oz. Carbon Fiber 5-Harness Satin Fabric

$52.44$142.98

SKU: W-CF-10.8-5HS

The 10.9 oz. Carbon Fiber is a high strength, five harness (5HS) satin weave fabric woven from 6K carbon fiber strands (tow).

Product Datasheet Icon

Description

The 10.8 oz. Carbon Fiber is a high strength, five harness (5HS) satin weave fabric woven from 6K carbon fiber strands (tow). The weave pattern creates a pliable fabric that easily conforms to contoured surfaces and compound curves while offering a highly decorative three-dimensional finish.

It is an excellent fabric for structural applications and builds up quickly. It offers fewer distortions and is easier to use than a twill weave. It produces a highly decorative three-dimensional finish.

It offers superior wet-out capability because it is sized with a coupling agent that provides a chemical bond between the carbon fiber and various resins. It is suitable for use in wet layup, vacuum bagging and resin infusion manufacturing and is compatible with polyester, vinyl-ester and epoxy resins.

Technical

Physical Properties

  • Weave: 5 Harness Satin Weave
  • Weight: 10.9 oz/yd²
  • Thickness: .028″
  • Fabric Count (Warp x Fill): 12 x 11.33
  • Warp Fiber: 6K Carbon Fiber Standard Modulus PAN, 33MSI
  • Fill Fiber: 6K Carbon Fiber Standard Modulus PAN, 33MSI

Technical Fiber Properties

  • Fiber: Carbon Fiber Standard Modulus PAN, 33MSI
  • Density: .064 lb/in³
  • Tensile Strength: 530 ksi
  • Tensile Modulus: 33.5 msi
  • Strain to Failure: 1.5%
  • Specific Tensile Strength: 8.33 106 in
  • Specific Tensile Modulus: 5.25 108 in
  • Coefficient of Thermal Expansion: -0.33 x 10-6/°F
  • Decomposition Temperature: 6632°F

Please note: All data to be used as a guide only; not a specification.


Documents

Product Datasheet Icon

Compatibility

  • Epoxy Resin
  • Polyester Resin
  • Vinyl-ester Resin