11.2 oz Carbon Fiber Fabric TW


SKU: W-CF-11.2-TW

ACP Composites’ 11.2oz 2×2 Twill fabric is woven with 6K carbon and builds up quickly. Is excellent for structural applications and conforms to curves.

Product Datasheet Icon


The 11.2 oz. Carbon Fiber is a high strength two-by-two weave fabric woven from 6K carbon fiber strands (tow). The twill weave pattern weave creates a highly flexible fabric that conforms to contoured surfaces and compound curves while offering the aesthetic of the 2×2 twill weave pattern. This fabric is not as drapable as the 3K twill due to increased stiffness.

It is an excellent fabric for lightweight applications and is most popular for use in decorative applications. Use this fabric to achieve that classic, decorative “carbon fiber” look on any project.

It offers superior wet-out capability because it is sized with a coupling agent that provides a chemical bond between the carbon fiber and various resins. It is suitable for use in wet layup, vacuum bagging and resin infusion manufacturing and is compatible with polyester, vinyl-ester and epoxy resins.



Product Datasheet Icon

Physical Properties

  • Style: 94910
  • Weave: 2×2 Twill Weave
  • Weight: 11.14 oz/yd²
  • Thickness: .016″
  • Fabric Count (Warp x Fill): 11 x 10.8
  • Warp Fiber: 6K Carbon Fiber Standard Modulus PAN, 33MSI
  • Fill Fiber: 6K Carbon Fiber Standard Modulus PAN, 33MSI

Technical Fiber Properties

  • Fiber: Carbon Fiber Standard Modulus PAN, 33MSI
  • Density: .064 lb/in³ Tensile Strength: 530 ksi
  • Tensile Modulus: 33.5 msi
  • Strain to Failure: 1.5% Specific
  • Tensile Strength: 8.33 106 in
  • Specific Tensile Modulus: 5.25 108 in
  • Coefficient of Thermal Expansion: -0.33 x 10-6/°F
  • Decomposition Temperature: 6632°F

Please note: All data to be used as a guide only; not a specification.